719781
カーボンナノファイバー
graphitized (iron-free), composed of conical platelets, D × L 100 nm × 20-200 μm
別名:
PR-25-XT-HHT, 円錐形炭素ナノファイバー
サイズを選択してください
この商品について
form
powder
greener alternative product characteristics
Design for Energy Efficiency
Learn more about the Principles of Green Chemistry.
sustainability
Greener Alternative Product
D × L
100 nm × 20-200 μm
surface area
24 m2/g
impurities
iron-free, <100 ppm Iron content
average diameter
130 nm
pore size
0.075 cm3/g average pore volume, 124 Å average pore diameter
mp
3652-3697 °C
density
1.9 g/mL at 25 °C
bulk density
0.5‑3.5 lb/cu.ft
greener alternative category
SMILES string
[C]
InChI
1S/C
InChI key
OKTJSMMVPCPJKN-UHFFFAOYSA-N
General description
Application
Preparation Note
Legal Information
Still not finding the right product?
Explore all of our products under カーボンナノファイバー
signalword
Warning
hcodes
Hazard Classifications
Eye Irrit. 2 - STOT SE 3
target_organs
Respiratory system
保管分類
11 - Combustible Solids
wgk
WGK 3
flash_point_f
Not applicable
flash_point_c
Not applicable
資料
炭素繊維強化複合材料を用いた3Dプリンティングについてご紹介します。積層造形法の一種である3Dプリンティングは、低コストかつ高い柔軟性を有する製造を小規模から中規模で実現できる可能性があるため、産学界の双方で急速に関心が高まっています。
Pyrograf®-III気相成長カーボンナノファイバー（CNF：carbon nanofiber）は、多層カーボンナノチューブ（MWCNT：multi-walled carbon nanotube）の一種であり、気相流動法（the floating catalyst method）で製造されます。
3D printing is a type of additive manufacturing that can be used to rapidly fabricate components with highly customizable geometries.
関連コンテンツ
組織工学では、損傷した組織を修復または置き換えるために、体内の微小環境を模倣して、足場、生きた細胞、生物学的活性分子から組織を構築します。
Tissue engineering fabricates tissues cultures from scaffolds, living cells, and biologically active molecules by simulating the microenvironment of the body to repair or replace damaged tissue.
Instructions